Res.J.Chem.Sci.___________________________________Research Journal of Chemical Sciences Vol. 1(2), 43-55, May (2011) ISSN 2231-606X International Science Congress Association 43 Study of Carbonization for Cashew Nut ShellSanger S.H., Mohod A.G., Khandetode Y.P., Shrirame H.Y. and Deshmukh A.S. Dept. of Elec. and other Energy Sources, College of Agri. Eng. and Tech. DBSKKV, INDIAAvailable online at: www.isca.in (Received 07th April 2011, revised 22nd April 2011, accepted 23rd April 2011)Abstract Cashew nut shell (CNS) was utilized for carbonization in developed prototype kiln. Prototype kiln was evaluated with direct and indirect methods and characteristics of CNS and CNS char were determined by proximate and ultimate analysis. The maximum CNS temperatures obtained inside the kiln during direct and indirect method were recorded as 452.2C and 458.8C respectively. Maximum oil percentage, charcoal percentage and ash percentage in direct method were observed as 21.1 per cent, 21.04 per cent and 3.34 per cent respectively whereas 23.8 per cent, 18.3 per cent and 1.27 per cent in indirect method respectively. Hydrogen content in CNS was found about 6 to 7 per cent and nitrogen content in CNS was found about 0.70 to 0.75 per cent. Oxygen content in CNS was observed about 29 to 31 percent. Carbon, hydrogen and nitrogen content of the CNS char were observed in the range of 73 to 76 per cent, 4 to 5 per cent and 1 to 2 per cent respectively. It was found that nitrogen content has increased in CNS char after the carbonization of CNS. Oxygen content in the CNS char gets reduced to 13 to 14 percent, which was comparatively very less than CNS.It was observed that indirect method is more suitable for carbonization than direct method for obtaining higher calorific value char and maximum fixed carbon percentage as found in cashew nut shell char as 60 per cent. Introduction In Konkan region the cashew (Anacardium occidentale L) is one of the major horticultural crops. Cashew is an important evergreen tropical crop. India is the largest producer, processor, exporter and second largest consumer of cashew in the world. Total area in India under cashew cultivation is about 8,54,000 hectare with annual production of 6,20,000 tones giving average productivity 820 kg/ha with highest productivity reported in Maharashtra (1500 kg/ha) from 1,73,601ha (Fig.1) under cultivation and produced 1,97,000 tones of raw cashew nut seeds through 2200-3650 cashew processing units. Production of Cashew nut shell in Koknan region is 20,000 metric tons as waste product obtained during deshelling of cashew kernels. When CNSL removed, deoiled shells are abundantly available as a biomass waste. The shell comprises some 50% of the weight of the raw nut, the kernel represents 25% and the remaining 25% consists of the natural CNSL6-8 and shell production of cashew nut shells may be estimated to 3,10,000 tones from available stats. The cashew nut shell has calorific value of 4252 kcal/kg and calorific value of CNSL is 40MJ/kg 10. The waste biomass generated in cashew processing is utilized as a substitute to wood fuel by making charcoal with carbonization process11. Biocarbons have been manufactured by man for more than 3800 years12 and are among the most important renewable fuels in use today. Carbonization process13 has added advantage over direct combustion of cashew nut shell. In direct combustion, vapors of an anacardic acid are released which may cause harm to eyes. Carbonization process of cashew nut shell produced char as well 25-30 per cent7,10 cashew nut shell liquid (CNSL) by weight. Industrial applications of the CNSL-based products14 are numerous and include fungicide, pesticide, insecticide15, brake linings16, paints and primers, foundry chemicals, lacquers, cements, and specialty coatings, resin17. Lately, the biological activities18 of the CNSL components have attracted Res.J.Chem.Sci._____________________________________________Research Journal of Chemical Sciences Vol. 1(2), 43-55, May (2011) ISSN 2231-606X International Science Congress Association 44 considerable attention in the areas of macrolide, plant growth, acid activity, wood preservative and pressure treatment activity. Much of the biological activity is attributed to the anacardic acids, which are the major constituents of the cashew nutshells, along with cardols.However, the major constituents of the technical CNSL, as it is obtained in the current industrial practice of roasting or hot oil bath methods19, are the cardols and cardanols. In the carbonization process, solid residues with increasing content of carbon element of higher activation energy20 are formed from organic material usually by pyrolysis in an inert atmosphere. Char preparation by this method will help in self-reliance of cashew processing unit for fuel supply with higher combustion efficiency. Keeping this view, the present study was undertaken. Material and Methods The cashew nut shell available in the cashew processing industry was selected as a major raw material for the carbonization process. The proximate21,7 and ultimate analysis of CNS was carried out to find out the fuel properties. In addition to CNS properties, carbonization processes were studied using metal kiln and tin boxes under direct and indirect process. Experimental set up for carbonization of cashew nut shell: The carbonization of CNS was carried22out in developed small capacity single drum kiln23, which accommodate about 5 kg cashew nut shells. The kiln (plate 1.a) was designed with 8 mm diameter holes for the perforations with outlet for the oil at the bottom and vent for the exhaust at the top (plate 1c). The size selected was suitable for small amount of burning, low cost and fabrication could be developed locally. Design detail specification of kiln is depicted in table 1. At the beginning, the small vent at the top and the oil collecting tube at bottom allowed the burning of the cashew nut shells, and then operated as the pyrolysis mode in a closed kiln without air. Kiln was evaluated with and without perforated hole. The selected small capacity kiln was used for direct carbonization process (plate 1.a). The eight of raw CNS was measured and filled the kiln with full capacity and burn directly. Various temperatures at different location under kiln, exhaust temperature of vent and oil collected from the bottom sump were observed periodically. Time require to complete carbonization process and amount of char remain in kiln was observed at the end of process. The detailed flow chart of carbonization processed used is shown in fig.2. Direct heating method of carbonization: Sample of the cashew nut shell was weighed and recorded. Developed kiln was checked for any leakage and which could not generate heat loss. The wire mesh grate was kept for support at the bottom of the kiln. The height of the great support was 6 cm above the bottom and would act as a convective heat media for the partial oxidation process, which would make heat, flow inside the kiln become more effective. Kiln was closed after placing the CNS for the carbonization; initial start up firing24 was done using loose grass25 that would transfer the heat to the CNS. Continuous observations were done to know the transfer of heat; the kiln air inlet size was adjusted based on the changes observed at the exhaust. Inside temperature of the CNS, outside temperature of the kiln and temperature of the exhaust fumes were recorded for the every 60 minutes. The time was recorded and the carbonization stage changes were noticed. The kiln was continuously observed to see the smoke colour change from blue to light blue, it found that all the CNS had turned to charcoal; during that stage the light blue smoke would become clearer. The kiln was allowed to cool down for 8 hours. After that, ash and char were separated, weighed and recorded. Indirect heating method of carbonization: Two small tin boxes having 0.3 kg capacity were selected for the indirect heating method of the carbonization (plate 1.b). The hole was made at the center of the tin box lid in order to remove the volatile matter and moisture associated with it. These tin boxes were placed inside the kiln and were surrounded by the cashew nut shells. Sample of the cashew nut shell were weighed and recorded. Prepared kiln was Res.J.Chem.Sci._____________________________________________Research Journal of Chemical Sciences Vol. 1(2), 43-55, May (2011) ISSN 2231-606X International Science Congress Association 45 checked for any leakage and which could generate heat loss. The wire mesh grate was kept for support at the bottom of the kiln; the height of the great support was 6 cm above the bottom and would act as a convective heat media for the partial oxidation process, which would make heat, flow inside the kiln become more effective. Kiln was closed after placing the CNS for the carbonization; initial start up firing was done using wood chips that will transfer the heat to the CNS. Continuous observations were done to know the transfer of heat; the kiln air inlet size was adjusted based on the changes observed at the exhaust. Inside temperature of the CNS, outside temperature of the kiln and temperature of the exhaust fumes was recorded for the every 60 minutes. Recorded the time and the carbonization stage changes were observed. The kiln was continuously observed for colour change of the smoke from blue to light blue as it direct heating method. Proximate analysis of CNS and its char: Determination of moisture content: About 1g of finely powdered air-dried sample was weighed in a crucible. The crucible was placed inside an electric hot air-oven, maintained at 105C. The crucible was allowed to remain in oven for 1 hour and then taken out (with the help of a pair of tongs), cooled in desiccators and weighed. Loss in weight (ASTMD-3173) was reported as moisture (on percentage-basis). (26) Moisture content, (% wb) = 1232wwww- - × 100 Where, w = weight of crucible, g = weight of crucible + sample, g = weight of crucible + sample, after heating, g Determination of volatile matter volatile matter: Volatile matter was determined by keeping the dried sample in a closed crucible at 600C for six minutes and then at 900C for another six minutes (ASTMD-3275). The difference in the weight duo to loss of volatiles was taken as the total volatile matter present in the biomass. Loss in weight was reported as volatile matter on percentage basis. Volatile matter (%) = 100Where, = weight of crucible + weight of sample before oven drying, g = weight of crucible + weight of sample before keeping in muffle furnace, g = weight of crucible + weight of sample after keeping in muffle furnace, g Determination of ash content: The residual coal in the crucible in was then heated without lid in a muffle furnace at 750 C for half hour for (ASTMD-3174). The crucible was then taken out, cooled first in air, then in desiccators and weighed. Heating, cooling and weighing was repeated, till a constant weight was obtained. The residue was reported as ash on percentage-basis. Ash content, (%) = 1798wwww- - × 100 Where, = weight of crucible + weight of sample before oven drying, g = weight of crucible + weight of sample before keeping in muffle furnace, g = weight of crucible + weight of sample after keeping in muffle furnace, g Determination of fixed carbon: The fixed carbon in percentage was calculated by difference. Fixed carbon (%) = 100 – % of (moisture content + volatile matter +ash) Procedure for determination of calorific value of the fuel by using the Oxygen Bomb Calorimeter: A known mass of the given sample was taken in clean crucible. The crucible was then supported over the ring. A fine magnesium wire, touching the fuel sample, was then stretched across the electrodes. The bomb lid was tightly screwed and bomb filled with oxygen 25 atmospheric pressure. The bomb was then lowered into copper calorimeter, containing a known mass of water. The stirrer was worked and initial temperature of the water was noted. The electrodes Res.J.Chem.Sci._____________________________________________Research Journal of Chemical Sciences Vol. 1(2), 43-55, May (2011) ISSN 2231-606X International Science Congress Association 46 are then connected to 6-volt battery and circuit completed. The sample burns and heat was liberated. Uniform stirring of water was continued and the maximum temperature attained was recorded, the experimental setup for determination of calorific value using Bomb calorimeter. The calorific value of the CNS and its char was determined by using Bomb Calorimeter. The calorific value of the CNS and its char was determined by using the following formula26. Calorific value (kcal/kg) = X Where, W = weight of water in calorimeter (kg), w = water equivalent of apparatus, 1 = initial temperature of water (C), 2 = final temperature of water (C), X = weight of fuel sample taken (kg) Ultimate analysis of CNS and char: Carbon, hydrogen, oxygen, nitrogen, and sulphur content of CNS and its char were found out under the ultimate analysis. The ultimate analysis is helpful in calculating heat balances in any process in which coal is used as fuel. Using the values of proximate analysis, ultimate analysis of CNS char could be done theoretically by using the various formulas27. Calculation of C, H, N and O from the proximate analysis: These values were carried out through the following steps27. Determination of carbon content: Carbon content of the sample was calculated theoretically on the basis of following formula, C = 0.97 FC + 0.7 (VM – 0.1 A) – M (0.6 – 0.01 M), % Determination of hydrogen content: Hydrogen content of the sample was calculated theoretically which was given by, H = 0.036 FC + 0.086 (VM – 0.1 A) – 0.0035 M (1 – 0.02 M), % Determination of nitrogen content: Nitrogen content of the sample was calculated theoretically which was given by, = 2.10 – 0.020 VM, % Determination of oxygen content: Oxygen content of the sample was calculated theoretically by difference on the basis of the following formula, = 100 - % of (C + H + N + Ash), % Where, FC = fixed carbon, % A = ash, % VM = volatile matter, % M = moisture, % Results and Discussion CNS was selected as a biomass for carbonization because CNS was treated as waste in Konkan region and it is abundantly available in this region. Bulk density of CNS was 481.83 kg/m, calorific value was nearly about 5000 kcal/kg and oil content was about 20 to 25 percent. The calorific values and oil content values were observed similar to values observed by Ramanan in 2008. Carbonization of CNS: In the carbonization process, solid residues with increasing content of the element carbon were formed from the organic material usually by pyrolysis in an inert atmosphere. Char preparation by this method would help in self reliance of cashew processing unit for fuel supply with higher combustion efficiency. The carbonization process of CNS was carried out in direct and indirect ways, which results into the production of charcoal (Plate 1 d) as the main product plus gaseous product along with the CNSL (Plate 1 e) and ash. For thorough study of the carbonization process, shell temperature inside the kiln, exhaust temperature at the top vent and the outside temperature of the cylinder were recorded. The temperatures recorded in the direct and indirect method are shown below in the graphical format in fig. 3 and fig. 4 respectively.It was observed from the fig. 3 and fig. 4 that time required to reach maximum temperature inside the kiln using indirect method was comparatively less than direct method for obtaining CNS char. maximum temperature was achieved in indirect Res.J.Chem.Sci._____________________________________________Research Journal of Chemical Sciences Vol. 1(2), 43-55, May (2011) ISSN 2231-606X International Science Congress Association 47 method in less time while direct method took more time for the carbonization. This may happen due as temperature of dried fuel was evaluated to about 225-325C, pyrolysis of hemicelluloses begins, cellulose gets pyrolysed at a temperature range of 325C –375C while legnin starts pyrolysing at a temperature range of 350-500C 28. Pyrolysis gases escape and char layer is form on fuel particle. It could be observed, in both methods, inside temperature varies more drastically than outside exhaust temperatures. Average temperature of shell at core part of kiln varies from 86 C to 445C in direct method whereas it varies from 80C to 448C in indirect method. Average exhaust temperature at the top vent varies from 172C to 218C in direct method while it varies from 175C to 230C in indirect method. Average outside temperature of the kiln was recorded in the range of 44C to 60C for direct method and 45 to 61C for indirect method. It was also observed that smoke colour gradually changes from blackish to white and then from white to colourless when all CNS turned to charcoal at the temperature 350C onwards in both the methods. Similarly, for comparing between the direct and indirect method, char percentage, oil percentage and ash percentage were observed and recorded which is shown graphically in fig. 5, fig. 6 and fig. 7 respectively. From the fig. 5, fig. 6 and fig. 7, it was observed that char and ash percentage obtained in direct method was more than indirect method and oil percentage obtained in direct plus indirect method was more compared to direct method. Maximum oil percentages obtained in direct and direct plus indirect method were recorded as 21.1 per cent and 23.8 per cent respectively. Properties of CNSL like flash and fire point; viscosity, pH and calorific value were determined (table 2) for safe handling, storage and use of CNSL on commercial scale. In direct method, maximum char and ash percentages were recorded as 21.04 per cent and 3.34 per cent respectively while in case of indirect method these values were recorded as 18.45 per cent and 1.27 per cent respectively. Charcoal obtained in indirect method was comparatively low than direct method but had more calorific value reason being higher temperature while heating of partial at lower rate to lower ultimate temperature favors char formation29. Ash obtained in indirect method was observed less than that of direct method. This happened due to the reason that flame did not come in direct contact with CNS in indirect method. Since, ash obtained was less in indirect method; it is therefore indirect method considered as more suitable for carbonization of CNS. Char obtained from prototype kiln was tested in improved chulhas for water boiling test. Most things are found, while burning the char (Plate 1.f) of cashew nut shell smoke was not produced as produced by burning the raw cashew nut shell in same chulhas. Proximate analysis of CNS and its char: Proximate analysi30of CNS and its char for determination of moisture content, volatile matter, ash content and fixed carbon was carried out. Calorific value of the raw material was determined using standard procedure. The results of proximate analysis and calorific value are shown in figure 8 and figure 9 respectively. From the figure 8, it was observed that moisture content of the CNS varies from 10 to 11% while moisture content in char varies from 5 to 6 %. For CNS the volatile matter observed in the range from 65 to 70% while in char varies from 25 to 30%. It could also be observed that ash content in the CNS sample was less than that of the CNS char. After carbonization fixed carbon percentage was found considerably increased in CNS char. From the figure 9, it was observed that maximum calorific value of char obtained in direct method was calculated as 6474.6 kcal/kg and char obtained in indirect method has maximum calorific value 6714.8 kcal/kg. Char obtained in indirect method was more superior to the char obtained in direct method due to its high calorific value31. Res.J.Chem.Sci._____________________________________________Research Journal of Chemical Sciences Vol. 1(2), 43-55, May (2011) ISSN 2231-606X International Science Congress Association 48 Ultimate analysis of CNS and its char: The ultimate analysis of CNS and its char was carried out in order to determine its carbon, hydrogen and oxygen and nitrogen percentage. Ultimate analysis of the given sample was carried out theoretically from the results obtained in proximate analysis. Ultimate analysis of the given sample could be carried out theoretically on the basis of formulae. The results of ultimate analysis of CNS and CNS char are shown graphically in figure10. From the figure 10 (a), it was found that carbon percentage in the CNS was in the range of 60 to 62 percent. Hydrogen content in CNS was found about 6 to 7 per cent and nitrogen content in CNS was found about 0.70 to 0.75 per cent. Oxygen content in CNS was observed about 29 to 31 percent. Similarly, from the figure 10 (b), carbon, hydrogen and nitrogen content of the CNS char were observed in the range of 73 to 76 per cent, 4 to 5 per cent and 1 to 2 per cent respectively. It was found that nitrogen content has increased in CNS char after the carbonization of CNS. Oxygen content in the CNS char gets reduced to 13 to 14 percent, which was comparatively very less than CNS. Mass and Energy balance: Actual amount of CNS char obtain in direct combustion after thermal decomposition in kiln comparing to raw CNS material was low but while analyzing carbon balancing depicted in figure 10 shows actual utilization of carbon was 28 % and it get lost 28.4 % carbon in exhaust gases, 17 % kg carbon in condensate, 0.6 kg in ash and remaining 26 % is un burn. That many losses occurred in condensate and exhaust gases due to evaporation of moisture and formation of CNSL oil, which required 2.8 MJ of energy to drive out one kilogram of moisture in fuel32There is large unaccounted heat loses due to several factor as heat energy loss itself due to the kiln heat losses in terms of startup energy as well as heat losses13 in direct combustion. The energy balance predicted the share of energy was 31 % in CNS char, rest of 23 % lost in exhaust, 14 % in condensate, 17 % in un burnt char and 14 % energy losses found as unaccounted. Conclusions It was observed that indirect method is more suitable for carbonization than direct method for higher calorific value char. It was observed that time required for the carbonization using indirect method was comparatively less than direct method. It was observed that maximum fixed carbon percentage found in cashew nut shell char as 60 per cent. Acknowledgements Authors are highly thankful to Department of Electrical and Other Energy Sources, College of Agricultural Engineering and Technology, DBSKKV, Dapoli for giving the facility to carry out research work. References 1.http://www.cashewindia.org(2017) 2.Haldankar P.M., Haldvnkar P.C., Govekar M.S. and Mali P.C., Cashew research and development in Konkan region of Maharashtra, Proceeding of National seminar on research, development and marketing of cashew, Goa, 33-35 (2007)3.Anonymous Cashew production technology. Technical Note, National Research Center for Cashew, ICAR, Puttur, Karnataka, 12-34 (2009)4.Mohod Atul, Jain Sudhir and Powar A.G., Energy option for small-scale cashew nut processing in India, Energy Research Journal,1,47-50 (2010)5.Belen B. Bisana and Nieva B. Laxamana, Utilization of cashew nut shell residue for charcoal briquettes and activated carbon production, Journal of Wood Science,44, 56-61 (2008) 6.Rajapakse R.A., Gunatillakeand P.A. and Wijekoon K.B., A Preliminary study on processing of cashew-nuts and production of cashew nut shell liquid (CNSL) on a commercial scale in Sri Lanka, J. Ntn. Sci. Coun.,5(2), 117-124 (1977)7.Venkata Ramanan M., Lakshmanan E., Sethumadhavan R. and Renganarayanan S., Performance prediction and validation of equilibrium modeling for Gasification of cashew nut shell char, Brazilian Journal of Chemical Engineering,25(3), 585-601 (2008)8.Maria Lucilia dos Santos and Gouvan C. de Magalhães, Utilisation of Cashew Nut Shell Liquid from Anacardium occidentale as Starting Material for Organic Snthesis: A Novel Route to Lasiodiplodin from Cardols, J. Braz. Chem. Soc., 10(1), 13-20, (1999)9.Tsamba Yang Weihong and Wlodzimierz Blasiak, Pyrolysis characteristics and global kinetics of coconut and cashew nut shells, Fuel Processing Technology,87, 523-530 (2006) 10.Das Piyali and Ganesh Anuradda, Bio-oil from pyrolysis of cashew nut shell-a near fuel, Biomass and Bioenergy, 25, 113-117 (2003)11.Das Piyali, Sreelatha T. and Anuradda G., Bio-oil from pyrolysis of cashew nut shell characterization and related properties, Biomass and Bioenergy,27, 265-275 (2004)12.Bard, E.Science, 292, 2443-2444 (2001)13.Kampegowda Rajesh and Chandayot Pongchan, Slow pyrolysis for rural small biomass energy by joint project development in Brazil and Thailand (2007) www.asianust.ac.th, 1-17. 14.Mathew Obichukwu, Labake and Ngozi Rita, Extraction of Polyphenols from Cashew Nut Shell, Leonardo Electronic Journal of Practices and Technologies, , 107-112 (2006)15.Behrens R., Cashew as an Agroforestry Crop, Tropical Agriculture, Margraf Verlag, Weikersheim, Germany (1996) 16.Lubi M.C. and Thachil E.T., Cashew nut shell liquid (CNSL)- a versatile monomer for polymer synthesis, International journal of polymeric materials, 3(2), 123-153 (2000)17.Oghome P. and Kehinde A.J., Separation of Cashew Nut Shell Liquid by column Cromatography, African Journal of Science and Technology, Science and engineering, 5(2), 92-95(2000)18.Shobha S.V. and Ravindranath B., Supercritical Carbon Dioxide and Solvent Extraction of the Phenolic Lipids of Cashew Nut (Anacardium occidentale) Shells., J. Agric. Food Chem.,39, 2214-2217 (1991)19.Tyman J.H.P., In Studies in Natural Products Chemistry, Atta-ur-Rahan, Ed., Elsevier Science Publisher, Amsterdam, , 313 (1991)20.Ro K.S., Cantrell K.B., Hunt P.G., Ducey T. F. Vanotti M.B. and Szogi A.A., Thermo chemical conversion of livestock waste: carbonization of swine solids, Journal of bioresearch Technology, 100, 5466-5471, (2009) 21.Singh R.N., Jena U., Patel J.B. and Sharma A. M., Feasibility study of cashew nut shell as an open core gasifier feedstock, Renewable Energy,31, 481-487 (2006)22.Anonymous, AMM, Murugappa Chettiar Research Center Taramani, Chenai, 3-4 (2008)23.Sjoerd Nienhuys Ing., The Beehive Charcoal Briquette Stove in the Khumbu Region, Nepal, 6-7 (2003)24.Jenkins B.M., Baxter L.L., Miles J and Miles T.R., Combustion properties of biomass, Fuel processing Technology, 54, 17-46 (1998) 25.Quaak P,Knowf H, and Stassen H. biomass: a review of combustion and gasification technologies, World Bank Technical paper Series No. 422, Washing World Bank, 178 (1999)26.Dara S.S., A practical handbook of Engineering Chemistry, 60-62 (1999)27.Anonymous, Notes f rom Bureau of Energy Efficiency (2008)28.Shafizadeh F. and Chin P.S. deterioration of Wood, In wood technology: chemistry aspects, edited by I S Gol Washington, DC:ACS press, 57- 81(2017) 29.Wenzl H., Rates of coal pyrolysis and gasification reactions. In coal conversion technology, edited by C. Y. Wen and E.S. Lee, 57-170 (1970)30.Curvers A. and Gigler J.K., Characterization of biomass fuel, an inventory of standard procedure for the determination of biomass properties ECN-C-96-032, 66 (1996)31.Cordero T., Marquez F. , Rodriguez and Rodriguez J.J., Predicting heating values of lignocelluloses and carbonaceous materials fr proximate analysis, Fuel,80, 1567(2017) 32.Kishor V.V.V.N., Renewable Energy Engineering and Technology , TERI Press, New Delhi, 717 (2008)