Research Journal of Chemical Sciences ______________________________________________ ISSN 2231-606X Vol. 2(8), 31-36, August (2012) Res.J.Chem.Sci. International Science Congress Association 31 Characterization of Bitumen and Modified Bitumen (e-PMB) using FT-IR, Thermal and SEM techniquesGupta Reena1*, Sangita and Kaur Verinder3 Dept. of Chemistry, Maharishi Ved Vyas Engg College, Jagadhri, INDIA Flexible Pavement Division, Central Road Research, New-Delhi, INDIA Guru Nanak Khalsa College, Yamunanagar, INDIAAvailable online at: www.isca.in Received 18th April 2012, revised 30th April 2012, accepted 23rd May 2012Abstract In last five years WEEE production increases to an alarming rate. At present, there are number of methods to manage it such as dismantling and recovering of reusable parts like costly metals and incineration, pyrolysis, recycling of plastic components and lastly disposal in landfilling etc. but some of these processes are energy consuming and are neither cost effective nor eco-friendly. Therefore, the present study focuses on the effective and sustainable management of e-plastic waste left after recovery of metallic portion from discarded E-gadgets. It deals with the development of modified binder from e-plastic waste with an aim to find an innovative technology for its effective use to produce bituminous mixes used for road construction and to minimize it in the environment. To meet this objective homogenous blend (e-PMB) of e- polymers and bitumen were prepared using an electrically operated stirrer. These blends are then characterized using FT-IR, Thermal and SEM techniques. Keywords: e-plastic waste, modified bitumen, e-PMB, TGA, SEM, FT-IR Introduction E-waste is one of the fastest growing waste streams today and is growing almost three times the rate of municipal waste, globally. The EPA (Environmental Protection Act) estimates that 29.9 million desktops and 12 million laptops were discarded in 2007. That’s over 112,000 computers discarded per day. The EPA report estimates that 31.9 computer monitors were discarded in 2007. As there is no separate collection of e-waste in India, no reliable figures are available as yet to quantify the e-waste generation. But according to toxics link, a Delhi-based non-government organization (NGO), says that India annually generates 1.5 billion worth of e-waste. The situation is alarming in India because almost all of it finds its way into the informal sector as there is no organized alternative available at presentIn accordance with the National Environmental Policy (NEP) and to address sustainable development concerns, there is a need to facilitate the recovery and/or reuse of useful materials from waste generated from a process and/or from the use of any material thereby, reducing the wastes destined for final disposal and to ensure the environmentally sound management of all materialsE-plastics account for about 15-22% of the weight of WEEE out of which one third is suitable for mechanical recycling and 2/3rd needs to dispose by other means. However, there are number of problems related with e-Plastic recycling such as plastic housings are made from ABS plastic may contain tetrabromobisophenol-A (TBBA), which is a brominated flame retardant6. Chloroparaffins have been used as softeners (i.e. additives to allow the plastic to remain flexible) in e-plastic. E-plastic is a mixed plastic has unacceptably poor mechanical, flow and thermal properties. As a consequence, recovered (but mixed) material cannot be reused to make new computer housings. The end products formed tend to be for low grade use such as dustbin sacks. More than 90% of this waste is currently land filledas it represents difficult to recycle the e-waste. On the other side, the deformation problem of roads has become even more severe and other solutions are now being implemented. New developments in mix design and the use of modified binders are being introduced. It is recognized that the performance limits of conventional bitumen have been reached for a certain category of roads and that the use of polymers in bituminous road binders provides a cost effective solution .Therefore, the modified binders have been developed by using e-plastic waste (10% ad 15%) to find its effective use to produce bituminous mixes used for road construction and to minimize it in the environment. This paper deals with interpretation of these modified binders using FT-IR, thermal and structural behavior and compared with plain (conventional) bitumen. Material and MethodsVG 30 bitumen obtained from Mathura Refinery was used. Keyboard of computer was dismantled very carefully to separate plastics from them. This plastic is termed as e-plastic. Thermal studies show that waste e-plastic degrades above 200C whereas bitumen melts around 110ºC and degrades above 175ºC. Therefore, blending of e-plastic and bitumen was carried at 160ºC. Required quantity of e-plastic modifiers was added to bitumen. Simultaneously a nominal quantity of additive was added to facilitate mixing of plastic into bitumen. Blending was done in an oven attached with a stirrer, which is controlled by a thermostat at a constant temperature. The mixture of polymers Research Journal of Chemical Sciences __________________________________________________________ ISSN 2231-606X Vol. 2(8), 31-36, August (2012) Res.J.Chem.SciInternational Science Congress Association 32 and bitumen was stirred using an electrically operated stirrer for about one hour to yield a homogeneous blend. These blends as well as base bitumen are characterized using FT-IR, Thermal and SEM techniques. Experimental Studies: Two modified binder formulations are prepared with 10% and 15% of e–plastic waste.These formulations are termed as e-PMB. FTIR (Fourier Transform Infrared Spectroscopy) of Modified Binder: FT-IR analysis was carried out using MB 3000 (Horizon) FT-IR analyzer. The wavelength range of the instrument is 485 to 8500 cm-1 with resolution better than 0.7 cm-1.The spectra are shown in figure 1-3. Thermal analysis of modified binder: Conventional (base) bitumen and modified bitumen were subjected to thermal studies. The test was carried out using EXSTAR TG/DTA 6300 thermogravimetric analyzer instrument. The resolution of this instrument is 0.02 g as a function of temperature. Runs were carried out linear heating 5C/ min from room temperature to 800C under nitrogen at a flow rate of 200 ml / min. TGA, DTG and DTA Curves obtained on e-PMB containing different quantity of e-plastic waste samples are given below in figure (4-6). SEM (Scanning Electron Microscopy): The instrument used for the study of the microscopic structure of base bitumen and modified bitumen is the LEO 435VP is a high-performance, variable pressure scanning electron microscope with a resolution of 4.0nm. Its 5 axis computer controlled stage is mounted in a specimen chamber measuring 300 x 265 x 190mm and can accommodate specimens weighing up to 0.5kg. Standard automated features include focus, stigmator, gun saturation, gun alignment, contrast and brightness. Results and DiscussionThree samples of bitumen containing 0, 10, and 15% of e-plastic waste were subjected to FT-IR studies. The FT-IR Spectra of these three samples are shown in figure 1-3. Figure-1 FT-IR Spectra of base bitumen i.e. containing 0% e-plastic waste modifier Figure-2 FT-IR Spectra of e-PMB containing 10% e-plastic waste modifier Research Journal of Chemical Sciences __________________________________________________________ ISSN 2231-606X Vol. 2(8), 31-36, August (2012) Res.J.Chem.SciInternational Science Congress Association 33 The comparison of peak position and intensities of various peaks appearing in the FT-IR spectra of base bitumen, e-plastic waste modifiers and the modified bitumen (e-PMB 10% and e-PMB 15%) reveal that the relative intensity of the peaks appearing in the region 3652-3631 cm-1 is lower than that in the e-plastic waste modifiers. This indicates that the free O-H group of polymeric species undergoes some type of interactions with bitumen i.e. the O-H group is no more in a free state completely. Another indication of structural changes in the bitumen on addition of e-plastic waste into base bitumen is disappearance of some peaks (which were very prominent in case of base bitumen) and appearance of some new peaks in the modified bitumen samples (e-PMB 10% and e-PMB 15%). Base bitumen has peak values at 2723 cm-1, 2677 cm-1,1727 cm-1 1589 cm-1 and a cluster of peaks in the region 1211 cm-1 -1026 cm-1 which disappear on modification of bitumen with polymer (e-PMB 10% and e-PMB 15%). Modified bitumen have some new peaks such as 1520 cm-1 (e-PMB 10% )and 1512 cm-1 (e-PMB 15%). However, the appearance of different peaks cannot be assigned with 100% accuracy due to lack of any probable suggestive structures. Here we are dealing with a complex matrix. Figure-3 FT-IR Spectra of e-PMB containing 15% e-plastic waste modifier Figure-4 TG, DTG and DTA curves for base bitumen at a heating rate 5C/ min in nitrogen atmosphere Temp Cel 800 700 600 500 400 300 200 100 DTA uV 80.00 60.00 40.00 20.00 0.00 -20.00 -40.00 -60.00 -80.00 TG % 200.0 180.0 160.0 140.0 120.0 100.0 80.0 60.0 40.0 20.0 DTG mg/min 1.00 0.50 0.00 -0.50 -1.00 -1.50 -2.00 -2.50 -3.00 -3.50 -4.00  \n  \r\n\n  \r  \r   \r   \r\n\n  \r  \r\n   \r  \n \r \n \r   \r\n Research Journal of Chemical Sciences __________________________________________________________ ISSN 2231-606X Vol. 2(8), 31-36, August (2012) Res.J.Chem.SciInternational Science Congress Association 34 The initial decomposition temperatures (IDT) of base bitumen and e-PMB formulations containing plastic waste 10% and 15% are 400, 380 and 370C and char yield at 798C decreased from 15.6 to 11.23%. Onset of decomposition Ti values indicated that e-PMB samples are thermally stable up to temperature 200C and are safe to use for production of bituminous mix during construction of roads because there will be no emissions up to application temperatures. However, at 400C percent weight loss increased from 18 to 41, which indicated that on increasing percentage of e-plastic modifier weight loss, also increases due to decomposition of polymeric components. The temperature at which maximum decomposition occurs decreased from 448-411C as observed from DTG curves on addition of 10% and 15% e-plastic modifier to base bitumen. The comparative decomposition data is shown in table 1. Thermal properties of bitumen and modified bitumen (e-PMB):Figure-5 TG, DTG and DTA curves for e-PMB 10% at a heating rate 5C/ min in nitrogen atmosphere Figure-6 TG, DTG and DTA curves for e-PMB 15% at a heating rate 5C/ min in nitrogen atmosphere Table-1 Test Data from TG, DTG and DTA thermograms of different samples at a heating rate 5C/ min in nitrogen atmosphere e-PMB samples containing e-plastic waste Onset of Decomposition C) Initial Decomposition TemperatureC) Char yield at 798C DTG peak maxima temperature C) DTA maxima C) Nature of DTA peak 0%289 400 15.6 448 475 Endo 10% 283 380 12.15 439 - - 15% 277 370 11.23 411 398 Endo Temp Cel 800 700 600 500 400 300 200 100 DTA uV 80.0 60.0 40.0 20.0 0.0 -20.0 -40.0 -60.0 -80.0 -100.0 -120.0 TG % 200.0 180.0 160.0 140.0 120.0 100.0 80.0 60.0 40.0 20.0 DTG mg/min 0.50 0.00 -0.50 -1.00 -1.50 -2.00 -2.50  \r  \r\n  \r\n\n  \r \n  \r\n  \r    \r \n \r  \n \r    \r  Temp Cel 800 700 600 500 400 300 200 100 DSC uW 30.00 20.00 10.00 0.00 -10.00 -20.00 -30.00 TG % 220.0 200.0 180.0 160.0 140.0 120.0 100.0 80.0 60.0 40.0 20.0 0.0 DTG mg/min 1.00 0.50 0.00 -0.50 -1.00 -1.50 -2.00 -2.50 -3.00 -3.50 -4.00 -4.50  \r   \r  \r  \r\n  \r  \r   \r\n  \r \n \r \n \r  \n  \r    \r  \r\n  Research Journal of Chemical Sciences __________________________________________________________ ISSN 2231-606X Vol. 2(8), 31-36, August (2012) Res.J.Chem.SciInternational Science Congress Association 35 Scanning Electron Microscopic studies (SEM) of bitumen and modified bitumen (e-PMB): Base bitumen and Modified bitumen (e-PMB) containing 10% and 15% of e-plastic waste were subjected to SEM test to check the dispersion of modifier in bituminous phase. The SEM photographs are shown in figure 7-12. These photographs indicate the dispersion of e-plastic into bituminous phase. This dispersion is more prominent in case of e-PMB containing 15% e-plastic waste. Figure-7 Figure-8 VG30 Plain Bitumen VG30 Plain Bitumen Figure-9 Figure-10 e-PMB binder containing 10% e-plastic modifier e-PMB binder containing 10% e-plastic modifier Figure-11 Figure-12 e-PMB binder containing 15% e-plastic modifier e-PMB binder containing 15% e-plastic modifier Research Journal of Chemical Sciences __________________________________________________________ ISSN 2231-606X Vol. 2(8), 31-36, August (2012) Res.J.Chem.SciInternational Science Congress Association 36 ConclusionFT-IR spectra of modified blends shows the disappearance of some peaks (which were very prominent in case of pure bitumen) and appearance of some new peaks in the modified bitumen samples (e-PMB 10% and e-PMB 15%) which indicates that structural changes occurs on addition of e-plastic waste into base bitumen. Such structural changes contribute for high performance of e-PMB. Thermal studies show that the degradation of modified binders occurs above 300C as there is hardly any weight loss occurs up to 300C. It also shows that the modified binders are safe to use during construction of roads because there will be no emissions up to application temperatures. The application temperature is normally 160C maximum at the time of production of bituminous mix. SEM studies show that e–plastic waste disperses well in bitumen phase resulting in plastic reinforced binders. This led to structural modification in bitumen, which will improve its physical and engineering properties. References1.SinhaSatish, Sustainable E-waste Management, Toxic link, Retrieved from: http://www.toxicslink.org/art-view.php?id=134 (2010)2. Sharma Pramila, Fulekar M.H. and Pathak Bhawan, E-Waste- A Challenge for Tomorrow, Res. J. Recent Sci.,1(3), 86-93, (2012) 3.Urban hazard: Mumbai choking on e-waste, Retrieved from:http://www.timesofindia.indiatimes.com/ NEWS/ India/Urban_hazard_Mumbai_choking_on_e-waste/ RssArticle/articleshow/1671262 (2012)4.Guidelines for Environmentally Sound Management of Electronic Waste, March 12, Retrieved from: http://www.cpcb.nic.in/e_Waste.php (2008) 5.Gupta Reena, Sangita and Kaur Verinder, Electronic Waste: A Case Study, Res. J. Chem. Sci.,1(9), 48-56 (2011) 6.A report by: Meinhardt Infrastructure and Environment Group for Environment Australia, Computer and Peripherals Material Project, (2001) Retrieved from: http://s3.amazonaws.com/zanran_storage/www.environment.gov.au/ContentPages/4014922.pdf(2001)7.Gupta Rakesh K., Electronics Recycling, Retrieved from: http://www.netl.doe.gov/publications/proceedings/01/indpartner/em5-4.pdf(2012)8.William J., Hall and Paul T. Williams, Fast pyrolysis of halogenated plastics recovered from waste computers, Energy and fuels ,1536-1549, (2006)9.Downes, M. J. W., Koole, R. C., Mulder, E. A. and Graham, W.E., Some Proven New Binders and their Cost Effectiveness, Proceedings of the VIIth AAPA International Asphalt Conference Brisbane, 119-132. August 7-11, (1998)